| Nylon 6 + MOS2 | Delrin | PEEK CNC | PVC | Teflon PTFE | Polyethylene | |
|---|---|---|---|---|---|---|
| Properties | ||||||
| Tensile breaking load | 75 MPa | 68 MPa | 101 MPa | 55 MPa | 35 MPa | 18 MPa |
| Modulus of elasticity | 1,7 GPa | 2,8 GPa | 4,4 GPa | 3 GPa | 0,8 GPa | 0,8 GPa |
| Elongation at break | 60 % | 28 % | 20 % | 10 % | 400 % | 50 % |
| Density | 1,14 g/cm^3 | 1,41 g/cm^3 | 1,31 g/cm^3 | 1,42 g/cm^3 | g/cm^3 | g/cm^3 |
| Hardness | ND Brinell | ND Brinell | Brinell | Brinell | Brinell | Brinell |
| Melting temperature | 235 °C | 175 °C | °C | °C | °C | °C |
| Features | ||||||
| Price range | € € € € € | € € € € € | € € € € € | € € € € € | € € € € € | € € € € € |
| Lead time | < 4 days | < 4 days | <3 days | <3 days | <2 days | <4 days |
| Quote | Quote | Quote | Quote | Quote | Quote | |